Mineral characteristics and associated mineralization of weathering crust from ankroet complex (K2ak) at Mat camp, Da Lat

Abstract

Section of weathering crust developed on the biotite granite (ankroet complex), distributed on high leveling surfaces 1400–1700 m of Miocene age (N1) at Trai Mat area and around Da Lat city. In terms of petrographic characteristics, this weathered shell section is full of zones: laterite, litoma, saprolite, and the original stone. On chemical-mineral characteristics: The results of synchronous processing of the results of chemical, thermal and jealous analysis ... on vertical sections shows, they belong to the form of fealsit formation (FeAlSi) with 4 types of shells: Fealsit / goethite-kaolinite-gibsit (FeAlSi / gt-kl-gb / N1), AlSiferit / (kaolinite-hydromica) -gibsit-goethit (AlSiFe / (kl-hmi) -gb-gt / N1), Sialit (actually receptors) / kaolinite-hydromica (SiAl / kl-hmi / N1) and Sialit (alkaline) / kaolinite rock-forming minerals (SiAl / kvtđ-kl / N1-Q). About microelements: concentrate in VPH compared to original stone: Cu: 1.8 – 3.3 times, Pb: 1 – 2 times, Mo: 0 – 2.83 times, most other elements were removed from the shell. Related minerals: Camp Mat, Da Lat Kaolin can be used as raw material for producing white bone tiles and birth materials. In this weathered shell section, there is a weathered shell of AlSiferite / (kaolinite-hydromica) -gibsit-goethite (AlSiFe / (kl-hmi) -gb-gt) which is a weathered clay-rich weathering product (gibsit up to 30 - 40%), developing on biotite granite at Mat camp - Da Lat area is often seen only in basalt weathering crust which is very rare in granite.

MỞ ĐẦU

Đối tượng nghiên cứu của công trình này là các thành tạo VPH phát triển trên đá granit biotit (phức hệ ankroet), phân bố trên các bề mặt san bằng cao 1400 – 1700 m tuổi Miocen (N ₁ ) ở khu vực Trại Mát và xung quanh thành phố Đà Lạt. Đây là một trong các thành tạo VPH chứa kaolin khá điển hình mà chưa được nhiều nhà địa chất quan tâm nghiên cứu. Vì vậy, các vấn đề về đặc điểm phong hóa, thành phần vật chất của mặt cắt VPH cũng như khoáng sản liên quan với các kiểu VPH ở vùng Trại Mát vẫn còn chưa được giải quyết thỏa đáng.

Các kết quả khảo sát địa chất VPH ở thực địa cùng với kết quả phân tích mẫu trong phòng thí nghiệm, các tài liệu thu được từ các nguồn tài liệu khác nhau, đã cho phép xem xét chi tiết hơn các đặc điểm vỏ phong hóa trên đá granit biotit vùng Trại Mát Đà Lạt.

PHƯƠNG PHÁP

Các khái niệm cơ bản

Theo phân loại kiểu VPH, trên cơ sở phân tích thành hệ địa hóa khoáng vật là dựa vào tổ hợp cộng sinh nguyên tố và tổ hợp cộng sinh khoáng vật chính tạo nên VPH trên các loại đá khác nhau phân bố trên một bề mặt địa hình xác định.

Thành hệ địa hóa VPH là một tổ hợp nguyên tố chủ đạo tạo nên sản phẩm phong hóa tồn tại dưới dạng một tổ hợp cộng sinh khoáng vật xác định hình thành trong cùng một điều kiện phong hóa. Tên gọi của thành hệ được gọi tên theo các nguyên tố chủ đạo: Feralit (FeAl), tổ hợp cộng sinh nguyên tố sắt và nhôm 1 .

Kiểu thành hệ địa hóa VPH là một tổ hợp nguyên tố tạo nên sản phẩm phong hóa, tồn tại dưới dạng tổ hợp cộng sinh khoáng vật được hình thành trong cùng điều kiện phong hóa được phát triển trên loại đá nhất định 1 .

Theo phân loại theo kiểu địa hóa khoáng vật, đơn vị phân chia là kiểu vỏ với mỗi kiểu vỏ được đặc trưng bởi một kiểu thành hệ VPH và một tổ hợp khoáng vật duy nhất xác định điều kiện phong hóa. Một kiểu thành hệ VPH có thể bao gồm nhiều kiểu vỏ 2 .

Để hoàn thành bài báo này, tác giả đã thu thập các tài liệu và mẫu phân tích sau:

Bản đồ địa chất (tờ Đà Lạt) tỷ lệ 1: 50.000; Bản đồ vỏ phong hóa (tờ Đà Lạt) tỷ lệ 1: 50.000, nhật ký địa chất của Bùi Thế Vinh (quyển số 7 đến quyển số 12) 2 ;

Mẫu phân tích hóa toàn phần (cho VPH): 23 mẫu; mẫu silicat (cho đá gốc tạo vỏ): 02 mẫu; mẫu phân tích nhiệt vi sai + rơn ghen (cho VPH): 23 mẫu; mẫu phân tích quang phổ định lượng gần đúng (cho VPH: 23 mẫu; đá gốc: 01 mẫu) 2 ;

Phương pháp xử lý lại kết quả mẫu phân tích

Tất cả các kết quả phân tích mẫu các loại được thu thập, các tác giả đã tiến hành xử lý lại một các đồng bộ theo các dạng sau: Xử lý các mẫu phân tích hóa toàn phần, hóa cơ bản-nhiệt-rơn ghen; Xử lý các mẫu phân tích quang phổ bán định lượng, quang phổ ICP 2 ;.

Phương pháp tổng hợp tài liệu, thành lập bản đồ VPH 3, 4

Thành lập mặt cắt đứng (mặt cắt chuẩn) cho VPH; Thành lập bản đồ VPH; Viết báo cáo.

KẾT QUẢ VÀ BÀN LUẬN

Đặc điểm mặt cắt vỏ phong hóa

Trong diện tích vùng nghiên cứu, các thành tạo VPH có mặt cắt nghiên tốt ở khu vực Trại Mát trên đá granit biotit (phức hệ Ankroet), với độ cao tuyệt đối địa hình 1400 - 1700m tuổi bề mặt san bằng là Miocen (N ₁ ). Mặt cắt VPH này là mặt cắt đầy đủ các đới: laterit, litoma, saprolit và đá gốc ( Figure 1 , Figure 2 ).

Đới laterit: Đới trên cùng của mặt cắt là các kết tảng sắt, bột sét màu nâu vàng loang lổ, dày 2 – 3 m; Đới litoma: gồm hai phần; phần trên: Sạn sỏi laterit bauxit màu nâu đỏ, sét kaolin màu trắng đục loang vàng, dày 2 – 5 m; phần dưới: kaolin sạch màu trắng đục còn tàn dư cấu trúc đá granit, dày 2 – 7 m; Đới saprolit: granit phong hóa hoàn toàn còn giữ nguyên cấu trúc, đôi khi còn sót các mảnh đá gốc, dày 3 – 5 m; Dưới cùng: Granit biotit nứt vỡ.

Figure 1 . Mặt cắt VPH vết lộ DL. 11704 Trại Mát Đà Lạt 2

Đặc điểm thạch địa hóa mặt cắt vỏ phong hóa

Trên cơ sở mặt cắt VPH, kết hợp với xử lý kết quả phân tích thu thập đã phân chia vùng nghiên cứu thành các kiểu vỏ phong hóa sau ( Table 1 , Table 2 , Figure 3 , Figure 4 , Figure 5 , Figure 6 ).

a. Kiểu vỏ Fealsit goethit-kaolinit-gibsit ( ): Thuộc đới laterit, trường thạch học laterit với kiểu tổ hợp khoáng vật là goethit-kaolinit-gibsit.

Thành phần hóa học (%): SiO ₂ 28,2; Al ₂ O ₃ 15,05; Fe ₂ O ₃ : 42,18; FeO: 0,3; TiO ₂ : 0,9; CaO: 0,18; MgO: 0,27; MnO: 0,02; Na ₂ O: 1,03; K ₂ O: 3,0.

Thành phần khoáng vật (%): Thạch anh (qu): 10; kaolinit (kl): 20; gibsit (gb): 20; goethit+hematit (gh+hm): 50.

Các nguyên tố vi lượng (%): Ti 0,5; Ga 0,002; Ni 0,02; V 0,02; Cu 0,01; Pb 0,01; Sn 0,005; Cr 0,02; Zr: 0,01; Zn: 0,03.

b. Kiểu vỏ alsiferit (kaolinit, hydromica)-gibsit-goethit ( ): Thuộc đới litoma, trường thạch học sét giàu kaolin với kiểu tổ hợp khoáng vật là (kaolinit, hydromica) -gibsit-goethit.

Thành phần hóa học (%): SiO ₂ 48,68 – 61,66, TB 52,48; TiO ₂ 0,49 – 1,09, TB 0,89; Al ₂ O ₃ 20,75 – 32,63, TB 27,85; Fe ₂ O ₃ 2,12 – 9,73, TB 4,85; Na ₂ O 0,0 – 0,75, TB 0,37; K ₂ O 0,07 - 4,30, TB 2,64; CaO 0,0 - 0,18, TB 0,07; MgO 0,08 - 1,45, TB 0,48.

Thành phần khoáng vật (%): qu: 12 - 40, TB 31; felspat (fp): 5; kl: 30 - 75, TB 38; hydromica (hmi): 5 - 15, Tb 7; gb: 5 - 25, TB 20; gh+hm: 2 - 20, TB 20.

Các nguyên tố vi lượng (%): V 0,001 - 0,02, TB 0,017; Ti 0,5 - 1,0, TB 0,56; Co: 0,01 - 0,03, TB 0,02; Ni 0,002 - 0,05, TB 0,08; Cr 0,02; Mo: 0,0003 - 0,001, TB 0,0005; Sn 0,001 - 0,01, TB 0,0056; As: 0,02 - 0,05, TB 0,04; Cu 0,005 - 0,01, TB 0,056; Ag: 0,00001 - 0,00002, TB 0,00001; Pb 0,002 - 0,01, TB 0,005; Zn: 0,003 - 0,01, TB 0,005; Ga 0,002 – 0,003, TB: 0,002; Be: 0,0001 – 0,0005, TB 0,0003; Nb: 0,001; Zr: 0,005 – 0,03, TB 0,02; La: 0,003 – 0,005, TB 0,003; Y: 0,001 – 0,02, TB 0,007; Yb: 0,0003 – 0,002, TB 0,0007; Se: 0,0005 – 0,001, TB 0,0009.

Khoáng sản liên quan: Sét kaolin làm nguyên liệu sản xuất gạch ốp lát loại xương trắng.

c. Kiểu vỏ sialit thực thụ kaolinit (kaolinit, hydromica) ( ): Thuộc đới litoma, trường thạch học sét kaolin với kiểu tổ hợp khoáng vật là kaolinit.

Thành phần hóa học (%): SiO ₂ 53,46 – 73,38, TB 63,47; TiO ₂ 0,11 – 0,59, TB 0,38; Al ₂ O ₃ 18,69 – 27,62, TB 23,49; Fe ₂ O ₃ 0,71 – 2,22, TB 1,39; FeO: 0,11 – 0,59, TB 0,38; Na ₂ O 0,08 – 0,13, TB 0,12; K ₂ O 0,38 – 4,30, TB 1,72; CaO 0,0 – 0,12, TB 0,05; MgO 0,0 – 0,7, TB 0,28; MnO 0,01 – 0,15, TB 0,05.

Thành phần khoáng vật (%): qu: 25 – 54, TB 36; fp: 5 – 10, TB 8; kl: 35 – 65, TB 45; hmi: 10 – 15, TB 13; gb: 0,0 – 20, TB 5; gh+hm: 1 – 5, TB 3.

Các nguyên tố vi lượng (%): V 0,02; Ti 0,5; Ni 0,002 – 0,05, TB 0,03; Cr 0,01; Mo: 0,001; Sn 0,005; Cu 0,005 – 0,01, TB 0,008; Ag: 0,00001; Pb 0,002 – 0,02, TB 0,01; Ga 0,002; Be: 0,0003; Nb: 0,001; Zr: 0,02 – 0,03, TB 0,025; La: 0,003; Y: 0,005; Yb: 0,0005; Se: 0,001.

Khoáng sản liên quan: Sét kaolin làm nguyên liệu sản xuất Sản xuất sứ vệ sinh.

d. Kiểu vỏ sialit kiềm khoáng vật tạo đá-kaolinit ( ): Thuộc đới saprolit, trường thạch học sét giàu kaolin với kiểu tổ hợp khoáng vật là khoáng vật tạo đá-kaolinit.

Figure 2 . Bản đồ vỏ phong hóa vùng Trại Mát, Đà Lạt 5 , 2

Thành phần hóa học (%): SiO ₂ 70,85 - 81,78, TB 75,44; TiO ₂ 0,11 – 0,21, TB 0,17; Al ₂ O ₃ 12,0 – 17,92, TB 15,66; Fe ₂ O ₃ 1,05 – 2,23, TB 1,52; FeO: 036 – 0,59, TB 0,49; Na ₂ O 0,03 – 0,28, TB 0,10; K ₂ O 0,10 – 4,48, TB 1,29; CaO 0,06 – 0,24, TB 0,15; MgO 0,0; MnO 0,01 – 0,03, TB 0,02.

Thành phần khoáng vật (%): qu: 40 – 64, TB 52; fp: 5 – 10, TB 7; muscovit (mus): 10; kl: 20 – 35, TB 29; hmi: 10 - 15, TB 12; gh+hm: 1 – 5, TB 3.

Các nguyên tố vi lượng (%): V 0,003 – 0,005, TB 0,02; Ti 0,3 – 0,05, TB 0,4; Ni 0,003 – 0,05, TB 0,012; Cr 0,003 – 0,05, TB 0,023; Mo: 0,0003 – 0,005, TB 0,003; Sn 0,001 – 0,02, TB 0,007; As: 0,03 – 0,05, TB 0,04; Cu 0,002 – 0,01, TB 0,005; Ag: 0,00001; Pb 0,002 – 0,005, TB 0,004; Zn: 0,003; Ga 0,002; Be: 0,0003; Nb: 0,001 – 0,002, TB 0,014; Zr: 0,01 – 0,03, TB 0,024; La: 0,003; Y: 0,005 – 0,01, TB 0,008; Yb: 0,0005 – 0,001, TB 0,0008; Se: 0,0003 – 0,005, TB 0,002.

Đá gốc tạo vỏ: granit biotit phức hệ Ankroet (K ₂ ak).

Thành phần hóa học (%): SiO ₂ 78,16; TiO ₂ 0,1; Al ₂ O ₃ 12,36; Fe ₂ O ₃ 0,8; FeO: 0,21; Na ₂ O 2,98; K ₂ O 4,88.

Thành phần khoáng vật (%): qu: 30; fp: 30, plagioclas: 30 - 35; biotit (bi)+muscovit (mus): 5 - 10; gh+hm: 1.

Các nguyên tố vi lượng (%): V 0,01; Ti 0,3; Ni 0,005; Cr 0,005; Mo: 0,01; Sn 0,01; Cu 0,003; Pb 0,005; Ga 0,002; Be: 0,003; Nb: 0,002; Zr: 0,02; La: 0,005; Y: 0,02; Yb: 0,002; Se: 0,0005.

Đặc điểm nguyên tố vi lượng vỏ phong hóa

Hành vi của các nguyên tố vi lượng so với đá gốc tạo vỏ ( Figure 3 ):

Đới laterit: các nguyên tố chỉ thị cho kim loại màu tập trung so đá gốc Cu:3,3 lần; Pb: 2 lần.

Đới litoma: Phần trên, các nguyên tố chỉ thị cho kim loại màu tập trung so đá gốc Cu: 1,8 lần, Pb: 1 lần; hầu hết các nguyên tố khác bị di chuyển khỏi vỏ.

Phần dưới, các nguyên tố chỉ thị cho kim loại màu tập trung so đá gốc Cu: 2,5 lần, Pb: 2,2 lần; hầu hết các nguyên tố khác bị di chuyển khỏi vỏ.

Đới saprolit: các nguyên tố chỉ thị cho kim loại màu tập trung so đá gốc Cu: 1,8 lần; nhóm nguyên tố kim loại hiếm tập trung so đá gốc Mo: 2,83 lần; còn hầu hết các nguyên tố khác bị di chuyển khỏi vỏ.

Figure 3 . Mặt cắt đứng VPH trên đá granit biotit khu vực Trại Mát, Đà Lạt (tỷ lệ 1: 100) 2

Table 1 Thành phần hóa học của mặt cắt VPH Trại Mát Đà Lạt 2

SHM	Thành phần các oxid (%)
	SiO2	Al2O3	Fe2O3	FeO	TiO2	CaO	MgO	MnO	Na2O	K2O
1- Đới laterit:
DL 11704	28,02	15,05	42,18	0,3	0,9	0,18	0,27	0,02	1,03	3,0
2- Đới litoma (phần trên)
DL11271	48,7	32,63	2,61	0,14	0,49		0,08	0,07
DL11272	50,22	20,75	4,37	0,17	0,75		1,45	0,2	0,02	0,1
DL11272/1	54,61	25,21	6,11	0,34	0,75		0,34	0,03		0,07
DL11703	52,0	31,3	2,73	0,27	0,99	0,06	0,44	0,01	0,28	4,3
DL11703/1	61,66	23,24	4,07	0,21	0,82	0,18		0,02	0,23	2,25
DL11703/2	52,47	30,73	2,12	0,16	1,01	0,06	0,31	0,02	0,75	3,53
DL11703/3	50,04	26,3	9,73	0,18	0,9	0,06	0,15	0,01	0,6	2,35
DL 11704/1	50,68	30,47	4,42	0,27	1,01	0,06	0,93	0,01	0,45	4,03
DL 11704/2	48,68	28,19	9,63	0,3	1,02	0,06	0,27	0,02	0,5	3,15
DL 11704/3	57,26	26,38	4,08	0,27	0,95	0,12	0,44	0,02	0,28	3,3
DL 11704/5	50,96	31,11	3,48	0,27	1,09	0,12	0,4	0,02	0,6	3,3
Min	48,68	20,75	2,12	0,14	0,49	0	0,08	0,01	0	0,07
Max	61,66	32,63	9,73	0,34	1,09	0,18	1,45	0,2	0,75	4,3
TB	52,48	27,85	4,85	0,23	0,89	0,07	0,48	0,04	0,37	2,64
- Đới litoma (phần dưới)
DL11271/1	53,46	27,62	1,3	0,11	0,55	0	0	0,07
DL 11271/2	59,24	27,49	0,71	0,34	0,32	0	0,51	0,15
DL 11704/4	58,8	26,24	1,35	0,59	0,99	0,12	0,7		0,08	4,3
DL 11704/6	73,38	18,69	1,73	0,3	0,17	0,06		0,01	0,13	0,38
DL 11704/9	68,7	20,37	1,0	0,49	0,1	0,06	0,08	0,01	0,13	0,95
DL 11704/10	67,24	20,55	2,22	0,46	0,12		0,09	0,02	0,13	1,25
Min	53,46	18,69	0,71	0,11	0,1	0	0	0,01	0,08	0,38
Max	73,38	27,62	2,22	0,59	0,99	0,12	0,7	0,15	0,13	4,3
TB	63,47	23,49	1,39	0,38	0,38	0,05	0,28	0,05	0,12	1,72
3- Đới saprolit
DL11703/4	81,78	12,0	1,05	0,36	0,11	0,18			0,05	0,1
DL11703/5	72,73	16,39	1,75	0,39	0,21	0,12	-		0,28	4,48
DL 11704/7	75,96	15,62	1,47	0,54	0,17			0,03	0,08	0,38
DL 11704/8	70,85	17,92	2,23	0,57	0,17	0,06		0,01	0,08	0,58
DL 11704/11	75,86	16,38	1,1	0,59	0,2	0,24			0,03	0,93
Min	70,85	12,0	1,05	0,36	0,11	0,06	0	0,01	0,03	0,1
Max	81,78	17,92	2,23	0,59	0,21	0,24	0	0,03	0,28	4,48
TB	75,44	15,66	1,52	0,49	0,17	0,15		0,02	0,1	1,29
4- Đới Đá gốc
DL11703/6	78,16	12,36	0,8	0,21	0,1				2,98	4,88

Table 2 Thành phần khoáng vật của mặt cắt VPH Trại Mát Đà Lạt 2

Mẫu	Thành phần khoáng vật (%)
	qu	fp	mus	kl	hmi	gb	Hm+gh
1- Đới laterit:
DL 11704	10			20		20	50
2- Đới litoma (phần trên)
DL11271	30			30	15	25
DL11272	30			45		5	20
DL11272/1	33			45		10	12
DL11703	30	5		30	5	25	5
DL11703/1	40	5		30	5	15	5
DL11703/2	30	5		30	5	25	5
DL11703/3	38	5		35		20	2
DL 11704/1	30	5		30	5	25	5
DL 11704/2	30	5		30	5	25	5
DL 11704/3	38	5		35		20	2
DL 11704/5	12	5		75			5
Min	12	5		30	5	5	2
max	40	5		75	15	25	20
TB	31	5		38	7	20	7
- Đới litoma (phần dưới)
DL11271/1	29			40	10	20	1
DL 11271/2	25			60	10		5
DL 11704/4	25	5		65			5
DL 11704/6	54	10		35			1
DL 11704/9	40	10		35	15
DL 11704/10	40	5		35	15		5
Min	25	5		35	10	20	1
Max	54	10		65	15	20	5
TB	36	8		45	13	20	3
3- Đới saprolit
DL11703/4	64	5		20	10		1
DL11703/5	50	5		30	10		5
DL 11704/7	54	10		35			1
DL 11704/8	40	5		35	15		5
DL 11704/11	53	10	10	25			2
Min	40	5	10	20	10		1
Max	64	10	10	35	15		5
TB	52	7	10	29	12		3
4- Đới Đá gốc
DL11703/6	54	10		35			1

Đặc điểm khoáng sản vỏ phong hóa

Table 3 So sánh thành phần Kaolin Trại Mát Đà Lạt với Tiêu chẩn Việt Nam: TCVN 6300: 1997 6 .

TT	Tên chỉ tiêu	Sứ vệ sinh	Gạch ốp lát loại xương trắng	Kaolin Trại Mát Đà Lạt		Ghi chú
				Đới Litoma trên (%)	Đới Litoma dưới (%)
1	Hàm lượng SiO2 (%)	50 – 70	50 – 70	52,48	63,47
2	Hàm lượng Al2O3(%)	≤ 19	≤ 19	27,85	23,49
4	Hàm lượng Fe2O3(%)	≤ 2	≤ 5	4,85	1,39
5	Hàm lượng SO3 (%)	≤ 0,5	≤ 0,5	0,00	0,00

Dựa vào tiêu chẩn Table 3 cho thấy, khoáng sản liên quan với Kaolin Trại Mát Đà Lạt gồm:

Đới Litoma trên (%), nguyên liệu sản xuất gạch ốp lát loại xương trắng;

Đới Litoma dưới (%), nguyên liệu sản xuất sứ vệ sinh;

Kaolin vùng Trại Mát đã được khai thác sử dụng từ lâu.

Figure 4 . Biểu đồ phân tướng địa hóa VPH trên đá trên đá granit biotit (phức hệ ankroet) ở khu vực Trại Mát và xung quanh thành phố Đà Lạt theo Nguyễn Thành Vạn (1986) 7 , Phạm Văn An và Đặng Thế Hùng (1992) 1 và Bùi Thế Vinh (2017) 8 .

Figure 5 . Biểu đồ phân trường thạch học VPH trên đá trên đá granit biotit (phức hệ ankroet) ở khu vực Trại Mát và xung quanh thành phố Đà Lạt theo Phạm Văn An và Đặng Thế Hùng (1992) 1 .

Figure 6 . Biểu đồ phân tướng khoáng vật VPH trên đá trên đá granit biotit (phức hệ ankroet) ở khu vực Trại Mát và xung quanh thành phố Đà Lạt theo Phạm Văn An và Đặng Thế Hùng (1992) 1

KẾT LUẬN

Các thành tạo VPH trên đá granit biotit (phức hệ Ankroet), với độ cao tuyệt đối địa hình ~ 1600m tuổi bề mặt san bằng là Miocen giữa (N ₁ ² ), mặt cắt VPH từ trên xuống có đầy đủ các đới phong hóa: laterit, litoma, saprolit và đá gốc. Trong đới litoma (phần trên) là kiểu vỏ alsiferit kaolinit-gibsit-goethit trên đá granit biotit khu vực Trại Mát Đà Lạt là minh chứng cho một kiểu mặt cắt VPH giàu nhôm (giàu gibsit) trên thực tế đã chứng minh sự phân tướng địa hóa VPH trên biểu đồ Nguyễn Thành Vạn (1986), Phạm Văn An (1992) và Bùi Thế Vinh (2017) là đúng đắn. Trong đới litoma (phần dưới) là kiểu vỏ phong hóa sialit - kaolin ở Trại Mát Đà Lạt tạo khoáng sản kaolin có giá trị công nghiệp đã được khai thác và sử dụng từ lâu, chúng là nguồn nguyên liệu khoáng để sản xuất gạch ốp lát loại xương trắng và sản xuất sứ vệ sinh. Các nguyên tố vi lượng hầu hết có sự linh động kém, một số nguyên tố chỉ thị cho kim loại màu tập trung so đá gốc Cu: 2,5 – 3,3 lần; Pb: 2,2 lần là khá thấp không có ý nghĩa khoáng sản.

Danh mục viết tắt

VPH: vỏ phong hóa; tuổi địa hình: N ₁ Miocen; N ₁ ² Miocen giữa.

qu: Khoáng vật thạch anh (qu); kl: Khoáng vật kaolinit; gb: Khoáng vật gibsit; gh Khoáng vật goethit; hm : Khoáng vật hematit; fp: khoáng vật felspat;: 30, pl: khoáng vật plagioclas; bi: khoáng vật biotit; mus: khoáng vật muscovit; kvtđ: khoáng vật tạo đá.

Các trường địa hóa: Si: trường silicite; Al: trường alit; Fe: trường ferit. SiAl: trường sialit; SiFe: trường siferit; AlFe: trường alferit; FeAl: trường feralit. SiAlFe: trường Sialferit; SiFeAl: trường sifealit; AlSiFe: trường alsiferit; AlFeSi: trường alfesit; FeAlSi: trường fealsit; FeSiAl: trường fesial; SiFeAl: trường sifeal; Fe-Si-Al: trường Ferosialit.

Cam kết không xung đột lợi ích

Tác giả xin cam kết, bài viết không xung đột lợi ích với các kết quả nghiên cứu và bài viết khác. Nếu xẩy ra xung đột lợi ích, tác giả xin hoàn toàn chịu trách nhiệm.

Đóng góp của các tác giả đối với bài báo

1. Bùi Thế Vinh (tác giả chính), chịu trách nhiệm về nội dung và chất lượng bài báo gồm: Thu thập các dạng tài liệu nhật ký địa chất, các sơ đồ, bản đồ địa chất và VPH, các kết quả phân tích mẫu hóa, mẫu nhiệt vi sai, mẫu rơn ghen và mẫu quang phổ định lượng gần đúng; Xử lý toàn bộ kết quả thu thập, thành lập các mặt cắt, các biểu đồ và bản đồ cho bài báo; Viết báo cáo chính, báo cáo tóm tắt, dịch sang tiếng Anh báo cáo tóm tắt. Ngoài ra, tác giả chính chịu trách nhiệm chỉnh sửa bài báo và trả lời các phản biện...

2. Trần Duy Phương (tham gia): Tham gia sử lý các kết quả mẫu phân tích; thành lập tài liệu tham khảo; thành lập danh mục các chữ viết tắt; nhập máy vi tính bài báo và kiểm tra toàn bộ lỗi chính tả, lỗi kỹ thuật.